Terblend N NM-11

Terblend® N NM-11 is an ABS/PA blend with excellent impact tougness and good flowability.

Key Features

  • High impact strength
  • Easy processing

Applications

  • Automotive parts
  • Ski toplayers
  • Helmets
  • Housings
  • Grade Version
  • Properties

    Properties of Terblend N NM-11

    Property, Test Condition Standard Unit Values
    Rheological Properties
    Melt Volume Rate, 240 °C/10 kg ISO 1133 cm³/10 min 30
    Mechanical Properties
    Tensile Modulus ISO 527 MPa 2000
    Tensile Stress at Yield, 23 °C ISO 527 MPa 43
    Tensile Strain at Yield, 23 °C ISO 527 % 3.5
    Nominal Strain at Break, 23 °C ISO 527 % > 50
    Flexural Modulus, 23 °C ISO 178 MPa 1800
    Flexural Strength, 23 °C ISO 178 MPa 62
    Charpy Notched Impact Strength, 23° C ISO 179/1eA kJ/m² 65
    Charpy Notched Impact Strength, -30 °C ISO 179/1eA kJ/m² 15
    Izod Notched Impact Strength, 23 °C ISO 180/A kJ/m² 65
    Izod Notched Impact Strength, -30 °C ISO 180/A kJ/m² 15
    Hardness, Ball Indentation ISO 2039-1 MPa 86
    Tensile Modulus after Moisture Absorption, Equilibrium 23 °C/50% RH ISO 527 MPa 1400
    Tensile Stress at Yield after Moisture Absorption, Equilibrium 23 °C/50% RH ISO 527 MPa 34
    Tensile Strain at Yield after Moisture Absorption, Equilibrium 23 °C/50% RH ISO 527 % 5.5
    Nominal Strain at Break after Moisture Absorption, Equilibrium 23 °C/50% RH ISO 527 % > 50
    Thermal Properties
    Vicat Softening Temperature VST/B/50 (50N, 50 °C/h) ISO 306 °C 102
    Vicat Softening Temperature, VST/A/50 (10N, 50 °C/h) ISO 306 °C 160
    Coefficient of Linear Thermal Expansion ISO 11359 10-6/°C 100
    Heat Deflection Temperature A; (unannealed; 1.8 MPa) ISO 75 °C 65
    Heat Deflection Temperature B; (unannealed; 0.45 MPa) ISO 75 °C 85
    Heat Deflection Temperature A; (annealed 4 h/80 °C; 1.8 MPa) ISO 75 °C 85
    Heat Deflection Temperature B; (annealed 4 h/80 °C; 0.45 MPa) ISO 75 °C 97
    Electrical Properties
    Relative Permittivity (1 MHz) IEC 60250 - 2.9
    Dissipation Factor (1 MHz) IEC 60250 10-4 150
    Volume Resistivity IEC 60093 Ω*m >1013
    Surface Resistivity IEC 60093 Ω 1014
    Other Properties
    Density ISO 1183 kg/m³ 1070
    Moisture Absorption, Equilibrium 23 °C/50% RH ISO 62 % 1.2
    UL94 rating at 1.5 mm thickness IEC 60695-11-10 - HB
    Processing
    Melt Temperature Range ISO 294 °C 240 - 270
    Mold Temperature Range ISO 294 °C 40 - 80
    Drying Temperature - °C 80 - 90
    Drying Time - h 4 - 8
    Molding shrinkage, free, longitudinal - % 0.7

    Typical values for uncolored products