Products

Terblend N 3154

Terblend® N 3154 is an 8% mineral filled ABS/PA blend with good dimensional stability and enhanced rigidity.

Key Features

  • High dimensional stability
  • Enhanced rigidity
  • Mineral filled (8%)

Applications

  • Housings of electrical devices
  • Grade Version
  • Properties

    Properties of Terblend N 3154

    Property, Test Condition Standard Unit Values
    Rheological Properties
    Melt Volume Rate, 260 °C/5 kg ISO 1133 cm³/10 min 8
    Mechanical Properties
    Tensile Modulus ISO 527 MPa 2700
    Tensile Stress at Yield, 23 °C ISO 527 MPa 55
    Tensile Strain at Yield, 23 °C ISO 527 % 2.9
    Nominal Strain at Break, 23 °C ISO 527 % 35
    Flexural Modulus, 23 °C ISO 178 MPa 2500
    Flexural Strength, 23 °C ISO 178 MPa 80
    Charpy Notched Impact Strength, 23° C ISO 179/1eA kJ/m² 8
    Charpy Notched Impact Strength, -30 °C ISO 179/1eA kJ/m² 6
    Charpy Unnotched Impact Strength, 23 °C ISO 579 kJ/m² 150
    Charpy Unnotched Impact Strength, -30 °C ISO 579 kJ/m² 100
    Izod Notched Impact Strength, 23 °C ISO 180/A kJ/m² 7
    Izod Notched Impact Strength, -30 °C ISO 180/A kJ/m² 5
    Thermal Properties
    Vicat Softening Temperature VST/B/50 (50N, 50 °C/h) ISO 306 °C 105
    Vicat Softening Temperature, VST/A/50 (10N, 50 °C/h) ISO 306 °C 130
    Heat Deflection Temperature A; (unannealed; 1.8 MPa) ISO 75 °C 83
    Heat Deflection Temperature B; (unannealed; 0.45 MPa) ISO 75 °C 97
    Coefficient of Linear Thermal Expansion ISO 11359 10-6/°C 80
    Heat Deflection Temperature A; (annealed 4 h/80 °C; 1.8 MPa) ISO 75 °C 93
    Heat Deflection Temperature B; (annealed 4 h/80 °C; 0.45 MPa) ISO 75 °C 100
    Electrical Properties
    Relative Permittivity (100 Hz) IEC 60250 - 3.4
    Relative Permittivity (1 MHz) IEC 60250 - 3.1
    Dissipation Factor (100 Hz) IEC 60250 10-4 150
    Dissipation Factor (1 MHz) IEC 60250 10-4 150
    Volume Resistivity IEC 60093 Ω*m 1013
    Surface Resistivity IEC 60093 Ω 1015
    Other Properties
    Density ISO 1183 kg/m³ 1110
    Moisture Absorption, Equilibrium 23 °C/50% RH ISO 62 % 1.3
    Filler Content (% Ash) - % 8
    UL94 rating at 1.5 mm thickness IEC 60695-11-10 - HB
    Processing
    Melt Temperature Range ISO 294 °C 240 - 270
    Mold Temperature Range ISO 294 °C 40 - 80
    Drying Temperature - °C 80 - 90
    Drying Time - h 4 - 8
    Molding shrinkage, free, longitudinal - % 0.6

    Typical values for uncolored products

  • Processing